Stainless Steel | Ferritic
1.4510 (439) Sheet and Plate
Stainless steel producers have an ongoing programme of development designed to produce new grades. These new grades are sometimes developed for specific end uses and sometimes to improve upon an existing grade.
Type 1.4510 spans both of these two areas since it was developed for a particular range of applications in certain industries where it can be used in place of type 1.4301 (304). On some aspects, its properties and performance in service are actually superior to 304 whilst on others it falls between 430 and 304. Notably however, it is also lower cost than 304.
Type 1.4509 can be referred to as a 'Super-Ferritic'
Features:
~ Good for Deep Drawing
~ Good Weldability
~ Good pitting corrosion resistance
~ Good brightness
~ Polishes well
Applications/Industries:
The main target sector is catering equipment to replace grade 304
Availability:
~ 1250mm & 1500mm wide
~ Thicknesses 0.5mm to 2.0mm
~ Finishes Bright Annealed or Polished
Chemical Composition
|
EN 10088-2:2005 1.4510 Steel |
|
|---|---|
| Chemical Element | % Present |
| Iron (Fe) | balance |
| Sulphur (S) | 0.02 max |
| Phosphorous (P) | 0.04 max |
| Carbon (C) | 0.05 max |
| Titanium (Ti) | 0.5 - 0.8 |
| Manganese (Mn) | 1 max |
| Silicon (Si) | 1 max |
| Chromium (Cr) | 16 - 18 |
Alloy Designations
Stainless Steel Grade 1.4510 is similar to, but may not be a direct equivalent to:
Type 439
UNS S43035
Uginox F18TNb
Sometimes referred to as 430LX.
Supplied Forms
- Sheet
- Plate
- Tube
Generic Physical Properties
| Physical Property | Value |
|---|---|
| Density | 7.70 g/cm³ |
| Melting Point | 1505 °C |
| Thermal Expansion | 11.0 x10^-6 /K |
| Modulus of Elasticity | 220 GPa |
| Thermal Conductivity | 25.0 W/m.K |
| Electrical Resistivity | 0.60 x10^-6 Ω .m |
Mechanical Properties
|
EN 10088-2:2005 Sheet & Plate - Up to 13.5mm Thick |
|
|---|---|
| Mechanical Property | Value |
| Proof Stress | 230 Min MPa |
| Tensile Strength | 420-600 MPa |
| Elongation A50 mm | 23 Min % |